NP-1002G Su Bazlı Akrilik İzolasyonlu ve Antikorozif Üst Kaplama

Model: NP-1002G
Sertifikasyon : ISO9001, ISO14001, ISO45001
Dağlamak: EKLEMLER
Yer: Guangzhou, Çin


NP-1002G is made of water-based acrylic emulsion as the film forming material, with titanium white powder, rust preventive and weatherproof pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Ürün kılavuzu
NP-1002G is made of water-based acrylic emulsion as the film forming material, with titanium white powder, rust preventive and weatherproof pigment, nano functional particle and other materials. Antirust pigments with high content of heavy metals, such as chromium and lead, are not added.
Ürün özelliği
  • Mükemmel hava direnci, UV direnci ve kendi kendini temizleme işlevi.
  • Excellent near-infrared and visible light reflection performance. When used together with thermal insulation intermediate coating such as NP-1002Z, it can provide very excellent thermal insulation effect.
  • Excellent resistance to acid, salt water and salt spray, with wide applicability.
Ana amaç
  • Korozyon önleyici ısı yalıtımlı üst kaplama olarak kullanılan, ısı yalıtım gereksinimleri olan yağ depolama tankı, petrol boru hattı, cihaz ve ekipmanın dış yüzeyine uygulanabilir.
teknik parametreler
Eşya Sonuç
Parıltı Mat
Renk Beyaz
Kütle katı içeriği (ana kaplama) Hakkında 54%
Teorik kaplama oranı 0.28 kg/ m2(70 mikron kuru film olarak ölçülmüştür)
Tack serbest zaman ≤2h (25℃, humidity 50%)
Tam kuruma süresi ≤24h (25℃, humidity 50%)
Yeniden kaplama süresi Minimum 2 saat, maksimum 48 saat (25 ° C)
Özgül ağırlık Hakkında 1.25 kg/L